Sample Info
- sample
Abomination
[1560403_A]
- sample_name
- Abomination
- sample_id
- 1560403_A
- details
E6 layer sample, 3-5 um, 4 mm x 4 mm
N-doped 99.999% 12C CVD layer (≈4-5 μm), as grown
EL SC substrate
Electron irradiated
Irradiated at PrismGem
Annealed in lab furnace at 800C for 12 hours
- Photo
- side 1
- side 2
- strain
- image_other1
- imager_other2
- location
- Pauli’s Setup
- user
- Pauli
- date
- user log
02/27/2018: Use in QDM 2.1 by Pauli
- impl.
- 4
- dose (cm^-2)
- energy (keV)
- 13C (%)
- N (cm^-3)
- 3.76e18
- N (ppm)
- NV (cm^-3)
- NV- (ppm)
- annealing temp. (C)
- 800
- annealing time (hours)
- 12
- annealing_history
Annealed in lab furnace
- irradiation
- Electron irradiated
- beam flux (1/cm^2 1/s)
- irradiation_time (hours)
- irradiation_history
Irradiated at PrismGem
- grower
- E6
- type
- 3
- layer thknss (μm)
- growth date
- dimen.
- 4 mm x 4 mm
- surface
- edge
- C (%)
- T2* (μs)
- max t2star
- T2 (μs)
- max t2
- T1 (ms)
- substr.
- CVD