Sample Info
- sample_name
- Tyrion
- sample_id
- 1660314-02
- details
E6 CVD on ELSC substrate
10 um 15N layer
99.99% 12CNV ~ 3 ppm (fluor. est.)
N ~ 10 ppm (from T2)
Sims data (for 14N, 12C, 13C only)Sides Polished DDK
Annealed at CfA
- Photo
- side 1
- side 2
- strain
- image_other1
- imager_other2
- location
- IDEA factory
- user
- Daniel
- date
- user log
6/9/23: With Daniel, in DM widefield setup.
5/25/23: In low field setup
4/7/23: borrowed by Daniel and Farhad for testing in the high field setup
April 2018: Sent to DDK for side polishing
Dec 2017: Being used by Hu Group for their studies (Diana)
Oct / Nov – Connor & Erik Spin Bath Driving Experiments
Aug 2016 – Connor & Erik characterized the sample
July 30, 2016 – Annealed at CfA (800 C soak and 1000 C soak)
- impl.
- dose (cm^-2)
- energy (keV)
- 13C (%)
- N (cm^-3)
- 1.76e18
- N (ppm)
- 10
- NV (cm^-3)
- 5.3E17
- NV- (ppm)
- 3
- annealing temp. (C)
- annealing time (hours)
- annealing_history
Annealed at 800C for 12 hours and 1000C for 12 hours
- irradiation
- beam flux (1/cm^2 1/s)
- irradiation_time (hours)
- irradiation_history
- grower
- E6
- type
- 3
- layer thknss (μm)
- 10
- growth date
- dimen.
- surface
- edge
- 1
- C (%)
- 8.8
- T2* (μs)
- 1.55
- max t2star
- 1.55
- T2 (μs)
- 15.7
- max t2
- 15.7
- T1 (ms)
- substr.
- CVD ELSC