Sample Info
- sample_name
- Jaime-D
- sample_id
- 1760308-02-D
- details
1.5 mm x 1.67 mm, 40 um layer on ELSC
10 ppm 15N
99.95% 12C (confirmed with E6)
irradiated 6e18e/cm^2 at 1MeV (Prism Gem) but not annealed
Brother to Cersei
Small piece cut off from 5 x 5 mm original diamond by DDK
- Photo
- side 1
- side 2
- strain
- image_other1
- imager_other2
- location
- IDEA Assembly Room; Storage Cabinet
- user
- NA
- date
- user log
05/30/2023 – realized this sample is not annealed so not much nv for setup calibration, put back in idea assembly storage cabinet
05/30/2023 – give to Reza for setup calibration
1/9/2018 – given to Jenny for spectroscopy
11/1/2017 – Connor for spin char
10/01/2017 – sent out for irradiation, returned
08/25/2017 – Given to Hu group for charge-state-ratio measurements
06/25/2107 – returned from being sliced at DDK
- impl.
- dose (cm^-2)
- energy (keV)
- 13C (%)
- N (cm^-3)
- N (ppm)
- NV (cm^-3)
- NV- (ppm)
- annealing temp. (C)
- annealing time (hours)
- annealing_history
- irradiation
- beam flux (1/cm^2 1/s)
- irradiation_time (hours)
- irradiation_history
- grower
- E6
- type
- 3
- layer thknss (μm)
- growth date
- dimen.
- 1×1
- surface
- edge
- C (%)
- T2* (μs)
- max t2star
- T2 (μs)
- max t2
- T1 (ms)
- substr.
- CVD ELSC