Sample Info
- sample_name
- Podrick
- sample_id
- 1860319-01
- details
Sample 1860319-1 with a ~5um thick, 1-3ppm [N] layers (we expect [Ns] to be around 2.5ppm), 99.999% 12C, 14N (natural abundance) on top of a ~100um pure (EL) layer grown on 1 small EL (2x2mm) substrate. This sample was meant to be used to determine the influence of a pure interlayer on the g=2 features.
T2: 80 us, DQ T2*: 4.4us
contrast (echo) is 1% (poor)
g=2 is minimal
Some surface issues (etch pits)
E6 irradiated and annealed
- Photo
- side 1
- side 2
- strain
- image_other1
- imager_other2
- location
- CfA Closet Diamond Box
- user
- Connor
- date
- user log
09/24/2018 – sample characterization, connor
- impl.
- dose (cm^-2)
- energy (keV)
- 13C (%)
- N (cm^-3)
- N (ppm)
- NV (cm^-3)
- NV- (ppm)
- annealing temp. (C)
- annealing time (hours)
- annealing_history
- irradiation
- beam flux (1/cm^2 1/s)
- irradiation_time (hours)
- irradiation_history
- grower
- type
- layer thknss (μm)
- growth date
- dimen.
- surface
- edge
- C (%)
- T2* (μs)
- max t2star
- T2 (μs)
- max t2
- T1 (ms)
- substr.
- CVD ELSC