Sample Info
- sample_name
- Kevan Lannister
- sample_id
- 1860320-03
- details
Samples 1860320-1 to 4 are ~2.5um thick, 1-3ppm [N] layers (we also expect [Ns] to be around 2.5ppm), 99.999% 12C, 15N grown on 2 small EL (2x2mm).
T2: 180us
DQ T2*: 8.9us
Contrast (echo) is 0.5% (very poor)
g=2 unknown (DEER-ESR not yet measured)
Some surface issues (etch pits)
13C rich interlayer with 300 ppb [N]
E6 irradiated and annealed
- Photo
- side 1
- side 2
- strain
- image_other1
- imager_other2
- location
- CfA Closet Diamond Box
- user
- date
- user log
08/08/2019 – pl-NMR: diamond glue testing.
- impl.
- dose (cm^-2)
- energy (keV)
- 13C (%)
- N (cm^-3)
- N (ppm)
- NV (cm^-3)
- NV- (ppm)
- annealing temp. (C)
- annealing time (hours)
- annealing_history
- irradiation
- beam flux (1/cm^2 1/s)
- irradiation_time (hours)
- irradiation_history
- grower
- type
- layer thknss (μm)
- growth date
- dimen.
- surface
- edge
- C (%)
- T2* (μs)
- max t2star
- T2 (μs)
- max t2
- T1 (ms)
- substr.