Sample Info
- sample_name
- Bizarro
- sample_id
- 1560404_A
- details
E6 layer sample. Targeted 25 ppm, 0.5-2 um, 4 mm x 4 mm
N-doped 99.999% 12C CVD layer (≈0.5-2 μm), as grown
EL SC substrate
Electron Irradiated
Linewidth (FWHM) ~650-700 kHz
[N] = 1.26 x 1018 cm-3
[N] = 7.2 ppm~10 large etch pits/pyramids
~1000s of tiny etch pits
- Photo
- side 1
- side 2
- strain
- image_other1
- imager_other2
- location
- CFA
- user
- Raisa
- date
- user log
02/2019: Matthew: Attempted use for phantom measurements, sides not polished, so sample is not usable
09/2018 – with Raisa for imaging new mw loops on QDM
08/27/2018: With Connor.
06/18/2018: Being used by Diana for PL strain measurements. (Idea that local strain influences the NV_- to NV_0 ratio.
-Notes: etch pits are everywhere on the sample and makes it not terribly usable
-Matthew: Growing cells on mount NRVM project
-Dominik: Using in NMR experiments for small sensing volume
-Matthew: Phantom Imaging Experiments
-Mikael’s setup
- impl.
- dose (cm^-2)
- energy (keV)
- 13C (%)
- N (cm^-3)
- 1.26e18
- N (ppm)
- 7.2
- NV (cm^-3)
- NV- (ppm)
- annealing temp. (C)
- annealing time (hours)
- annealing_history
- irradiation
- beam flux (1/cm^2 1/s)
- irradiation_time (hours)
- irradiation_history
- grower
- E6
- type
- 3
- layer thknss (μm)
- growth date
- dimen.
- 4 x 4 mm
- surface
- edge
- C (%)
- T2* (μs)
- 0.545
- max t2star
- T2 (μs)
- max t2
- T1 (ms)
- substr.
- CVD ELSC